Environmentally Friendly Surface Modification Treatment of Flax Fibers by Supercritical Carbon Dioxide - Université de Bourgogne Accéder directement au contenu
Article Dans Une Revue Molecules Année : 2020

Environmentally Friendly Surface Modification Treatment of Flax Fibers by Supercritical Carbon Dioxide

Résumé

The present work investigates the effects of an environmentally friendly treatment based on supercritical carbon dioxide (scCO2) on the interfacial adhesion of flax fibers with thermoset matrices. In particular, the influence of this green treatment on the mechanical (by single yarn tensile test), thermal (by TGA), and chemical (by FT-IR) properties of commercially available flax yarns was preliminary addressed. Results showed that scCO2 can significantly modify the biochemical composition of flax fibers, by selectively removing lignin and hemicellulose, without altering their thermal stability and, most importantly, their mechanical properties. Single yarn fragmentation test results highlighted an increased interfacial adhesion after scCO2 treatment, especially for the vinylester matrix, in terms of reduced debonding and critical fragment length values compared to the untreated yarns by 18.9% and 15.1%, respectively. The treatment was less effective for epoxy matrix, for which debonding and critical fragment length values were reduced to a lesser extent, by 3.4% and 3.7%, respectively.
Fichier principal
Vignette du fichier
molecules-25-00438-v2.pdf (12.68 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-02464475 , version 1 (19-07-2020)

Identifiants

Citer

Maria Carolina Seghini, Fabienne Touchard, Laurence Chocinski-Arnault, Vincent Placet, Camille François, et al.. Environmentally Friendly Surface Modification Treatment of Flax Fibers by Supercritical Carbon Dioxide. Molecules, 2020, 25 (3), pp.438. ⟨10.3390/molecules25030438⟩. ⟨hal-02464475⟩
116 Consultations
29 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More