UV accelerated aging of unidirectional flax composites: Comparative study between recycled and virgin polypropylene matrix

Résumé

Previous studies on the photooxidation of natural fiber composites have focused on using short fibers and virgin matrices. In this work, unidirectional flax fiber composites with virgin and recycled polypropylene matrix were prepared by thermocompression to compare their accelerated aging. These composites were exposed to two accelerated xenon arc UV exposures where only the irradiance was modified. A multi-scale characterization was carried out to evaluate the consequences of the photooxidation on their mechanical and physicochemical properties with time. Results show that the photooxidation was limited to the surface. In addition, the photo-degradation of the surfaces of both composites was identified by the appearance of cracks, the variation of crystallinity, the decrease in weight average molar mass, and the appearance of new chemical products. These physicochemical variations are more evident with increasing irradiance. Despite these variations, the mechanical tensile properties of recycled matrix composites remain relatively indifferent to the two UV exposures compared to those with virgin polypropylene. It can be concluded that recycled polypropylene, if well selected, can replace virgin polypropylene in natural fiber composites for better mechanical resistance to photooxidation.
Fichier non déposé

Dates et versions

hal-03971109 , version 1 (03-02-2023)

Identifiants

Citer

Lara Alam, Benoit Piezel, Olivier Sicot, Shahram Aivazzadeh, Sandrine Moscardelli, et al.. UV accelerated aging of unidirectional flax composites: Comparative study between recycled and virgin polypropylene matrix. Polymer Degradation and Stability, 2023, 208, pp.110268. ⟨10.1016/j.polymdegradstab.2023.110268⟩. ⟨hal-03971109⟩
37 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More